ISO 6721:2019
ISO 6721:2019 Plastics – Determination of dynamic mechanical properties – Part 8: Longitudinal and shear vibration – Wave-propagation method
CDN $131.00
Description
This document describes an ultrasonic wave propagation method for determining the storage components of the longitudinal complex modulus L* and the shear complex modulus G* of polymers at discrete frequencies typically in the range 0,5 MHz to 5 MHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 1 MHz. With materials that have a higher loss, significant errors in velocity measurement are introduced through waveform distortion and can only be reduced using procedures that are outside the scope of this document.
The method allows measurements to be made on small specimens, typically 50 mm √ó 20 mm √ó 5 mm, or small regions of larger specimens or sheets. It is therefore possible to obtain information on the homogeneity or anisotropy (see 10.5) of modulus in a specimen.
Edition
2
Published Date
2019-04-11
Status
PUBLISHED
Pages
11
Language
English
Format
Secure PDF
Secure – PDF details
- Save your file locally or view it via a web viewer
- Viewing permissions are restricted exclusively to the purchaser
- Device limits - 3
- Printing – Enabled only to print (1) copy
See more about our Environmental Commitment
Abstract
This document describes an ultrasonic wave propagation method for determining the storage components of the longitudinal complex modulus L* and the shear complex modulus G* of polymers at discrete frequencies typically in the range 0,5 MHz to 5 MHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 1 MHz. With materials that have a higher loss, significant errors in velocity measurement are introduced through waveform distortion and can only be reduced using procedures that are outside the scope of this document.
The method allows measurements to be made on small specimens, typically 50 mm √ó 20 mm √ó 5 mm, or small regions of larger specimens or sheets. It is therefore possible to obtain information on the homogeneity or anisotropy (see 10.5) of modulus in a specimen.
Previous Editions
Can’t find what you are looking for?
Please contact us at:
Related Documents
-
ISO 4589:2017 Plastics – Determination of burning behaviour by oxygen index – Part 2: Ambient-temperature test
CDN $310.00 Add to cart -
ISO 22766:2020 Plastics – Determination of the degree of disintegration of plastic materials in marine habitats under real field conditions
CDN $195.00 Add to cart -
ISO 22526:2020 Plastics – Carbon and environmental footprint of biobased plastics – Part 2: Material carbon footprint, amount (mass) of CO2 removed from the air and incorporated into polymer molecule
CDN $131.00 Add to cart -
ISO 5677:2023 Testing and characterization of mechanically recycled polypropylene (PP) and polyethylene (PE) for intended use in different plastics processing techniques
CDN $86.00 Add to cart