ISO 12732:2006
ISO 12732:2006 Corrosion of metals and alloys – Electrochemical potentiokinetic reactivation measurement using the double loop method (based on Cihal’s method)
CDN $193.00
Description
ISO 12732:2006 specifies the method for measuring the degree of sensitization (DOS) in stainless steel and nickel-based alloys using the Double Loop Electrochemical Potentiokinetic Reactivation (DL-EPR) test (based on Cihal’s method).
The method may be used for the quantitative assessment of deleterious thermal effects resulting in the formation of alloy-element-depleted zones at grain boundaries or in the matrix. However, attention should be paid when testing heat-affected weld zones, due to possible non-uniform distribution of sensitized zones along the fusion lines.
The results of the test can be used as an index to identify the potential susceptibility of stainless steel and nickel-based alloys to intergranular corrosion, pitting corrosion, and intergranular-stress corrosion cracking, but prediction of these corrosion modes depends on complementary specific testing.
ISO 12732:2006 describes the general methodology and gives examples of suitable test exposure conditions for specific alloys.
Edition
1
Published Date
2006-09-01
Status
PUBLISHED
Pages
14
Language
English
Format
Secure PDF
Secure – PDF details
- Save your file locally or view it via a web viewer
- Viewing permissions are restricted exclusively to the purchaser
- Device limits - 3
- Printing – Enabled only to print (1) copy
See more about our Environmental Commitment
Abstract
ISO 12732:2006 specifies the method for measuring the degree of sensitization (DOS) in stainless steel and nickel-based alloys using the Double Loop Electrochemical Potentiokinetic Reactivation (DL-EPR) test (based on Cihal's method).
The method may be used for the quantitative assessment of deleterious thermal effects resulting in the formation of alloy-element-depleted zones at grain boundaries or in the matrix. However, attention should be paid when testing heat-affected weld zones, due to possible non-uniform distribution of sensitized zones along the fusion lines.
The results of the test can be used as an index to identify the potential susceptibility of stainless steel and nickel-based alloys to intergranular corrosion, pitting corrosion, and intergranular-stress corrosion cracking, but prediction of these corrosion modes depends on complementary specific testing.
ISO 12732:2006 describes the general methodology and gives examples of suitable test exposure conditions for specific alloys.Previous Editions
Can’t find what you are looking for?
Please contact us at:
Related Documents
-
ISO 6509:2017 Corrosion of metals and alloys – Determination of dezincification resistance of copper alloys with zinc – Part 2: Assessment criteria
CDN $85.00 Add to cart -
ISO 16151:2018 Corrosion of metals and alloys – Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions
CDN $261.00 Add to cart -
ISO 8044:2024 Corrosion of metals and alloys – Vocabulary
CDN $261.00 Add to cart -
ISO 22410:2020 Corrosion of metals and alloys – Electrochemical measurement of ion transfer resistance to characterize the protective rust layer on weathering steel
CDN $193.00 Add to cart